繊維名	標準引張強さ(g/d)	湿潤引張強さ(g/d)
　※S:短繊維,F:長繊維

綿(ｱｯﾌﾟﾗﾝﾄﾞ)	3.0~4.9	3.3~6.4
麻(亜麻)	5.6~6.3	5.8~6.6
麻(ﾗﾐｰ)	6.5	7.7
毛(ﾒﾘﾉ)	1.0~1.7	0.76~1.63
絹	3.0~4.0	2.1~2.8
ﾚｰﾖﾝ S 普通	2.5~3.1	1.4~2.0
ﾚｰﾖﾝ S 強力	3.6~4.2	2.7~3.3
ﾚｰﾖﾝ F 普通	1.7~2.3	0.8~1.2
ﾚｰﾖﾝ F 強力	3.4~5.2	2.5~4.1
ﾎﾟﾘﾉｼﾞｯｸ S	3.8~5.2	2.8~4.2
ｷｭﾌﾟﾗ  S	2.9~3.4	2.0~2.5
ｷｭﾌﾟﾗ F	1.8~2.7	1.1~1.9
ｱｾﾃｰﾄ S	1.3~1.6	0.8~1.0
ｱｾﾃｰﾄ  F	1.2~1.4	0.7~0.9
ﾄﾘｱｾﾃｰﾄ F	1.2~1.4	0.8~1.0
ﾌﾟﾛﾐｯｸｽ F	3.5~4.5	3.2~4.2
ﾋﾞﾆﾛﾝ S 普通	4.0~6.5	3.2~5.2
ﾋﾞﾆﾛﾝ S 強力	6.8~10.5	5.3~9.0
ﾋﾞﾆﾛﾝ F 普通	3.0~4.0	2.1~3.2
ﾋﾞﾆﾛﾝ F 強力	6.0~12.0	5.0~10.5
ﾅｲﾛﾝ6 S	4.5~7.5	3.7~6.4
ﾅｲﾛﾝ6 F 普通	4.8~6.4	4.2~5.9
ﾅｲﾛﾝ6 F 強力	6.4~10.0	5.9~8.5
ﾅｲﾛﾝ66 F 普通	5.0~6.5	4.5~6.0
ﾅｲﾛﾝ66 F 強力	6.5~10.0	6.0~9.0
ﾋﾞﾆﾘﾃﾞﾝ S	0.9~1.5	0.9~1.5
ﾋﾞﾆﾘﾃﾞﾝ F	1.5~2.6	1.5~2.6
ﾎﾟﾘ塩化ﾋﾞﾆﾙ S 普通	2.0~2.8	2.0~2.8
ﾎﾟﾘ塩化ﾋﾞﾆﾙ S 強力	3.3~4.0	3.3~4.0
ﾎﾟﾘ塩化ﾋﾞﾆﾙ F	2.7~3.7	2.7~3.7
ﾎﾟﾘｴｽﾃﾙ S	4.7~6.5	4.7~6.5
ﾎﾟﾘｴｽﾃﾙ F 普通	4.3~6.0	4.3~6.0
ﾎﾟﾘｴｽﾃﾙ F 強力	6.3~9.0	6.3~9.0
ｱｸﾘﾙ S	2.5~5.0	2.0~4.5
ｱｸﾘﾙ F	3.5~5.5	3.2~5.5
ｱｸﾘﾙ系 S	2.2~4.0	2.0~4.0
ﾎﾟﾘｴﾁﾚﾝ(低圧法) F	5.0~9.0	5.0~9.0
高強度超高分子量ﾎﾟﾘｴﾁﾚﾝ F	25~50	25~50
ﾎﾟﾘﾌﾟﾛﾋﾟﾚﾝ S	4.5~7.5	4.5~7.5
ﾎﾟﾘﾌﾟﾛﾋﾟﾚﾝ F 普通	4.5~7.5	4.5~7.5
ﾎﾟﾘﾌﾟﾛﾋﾟﾚﾝ F 強力	7.5~9.0	7.5~9.0
ﾎﾟﾘｳﾚﾀﾝ(ｽﾊﾟﾝﾃﾞｯｸｽ) F	0.6~1.2	0.6~1.2
ﾎﾟﾘｸﾗｰﾙ      S	2.8~3.3	2.0~2.3
PBT(ﾎﾟﾘｴｽﾃﾙ) F	3.0~5.0	3.0~5.0
芳香族ﾅｲﾛﾝ(ｱﾗﾐﾄﾞ) S	4.5~5.5	3.6~4.7
全芳香族ﾎﾟﾘｴｽﾃﾙ(ﾎﾟﾘｱﾘﾚｰﾄ) F 普通	25~28	25~28
ﾌｪﾉｰﾙ系(ﾉﾎﾞﾛｲﾄﾞ) S	1.4~1.8	1.2~1.6
炭素繊維 F ﾋﾟｯﾁ系	3.2~22(50~350kg/mm^2)
炭素繊維 F PAN系	16~46(250~720kg/mm^2)
ﾌｯ素繊維 F	1.0~2.5	1.0~2.5

※参考文献：繊維学会編，「第２版　繊維便覧」，丸善(1994)